ASTM A106 Seamless Carbon Steel Tubes for High-Temperature Fluid Transport: Production and Applications by Womic Steel

Introduction

ASTM A106 steel pipe is a seamless carbon steel pipe for high-temperature service. Womic Steel, a leading manufacturer of ASTM A106 steel pipes, offers high-quality products with reliable performance. This article provides a detailed overview of the production dimensions, production process, surface treatment, packaging and transportation methods, testing standards, chemical composition, mechanical properties, inspection requirements, and application scenarios of ASTM A106 steel pipes by Womic Steel.

Production Dimensions

ASTM A106 steel pipes produced by Womic Steel have the following dimensions:

- Outer Diameter: 1/2 inch to 36 inch (21.3mm to 914.4mm)

- Wall Thickness: 2.77mm to 60mm

- Length: 5.8m to 12m (customizable)

Production Process

Womic Steel uses a hot-finished or cold-drawn seamless manufacturing process to produce ASTM A106 steel pipes. This process involves:

1. Selecting high-quality raw materials

2. Heating the raw materials to a suitable temperature

3. Piercing the heated billet to form a hollow tube

4. Rolling or extruding the tube to the desired dimensions

5. Heat treatment to improve mechanical properties

6. Finishing operations to achieve the final dimensions and surface finish

asd (1)

Surface Treatment

ASTM A106 steel pipes produced by Womic Steel can be supplied with various surface finishes, including:

- Black Painting

- Varnish Coating

- Galvanizing

- Anti-corrosion Coating

Packaging and Transportation

ASTM A106 steel pipes produced by Womic Steel are typically bundled or packaged in wooden cases for transportation. Special packaging requirements can be accommodated upon request.

Testing Standards

ASTM A106 steel pipes produced by Womic Steel are tested according to the following standards:

- ASTM A450/A450M: Standard Specification for General Requirements for Carbon and Low Alloy Steel Tubes

- ASTM A106/A106M: Standard Specification for Seamless Carbon Steel Pipe for High-Temperature Service

Chemical Composition

The chemical composition of ASTM A106 steel pipes produced by Womic Steel is as follows:

- Carbon (C): 0.25% max

- Manganese (Mn): 0.27-0.93%

- Phosphorus (P): 0.035% max

- Sulfur (S): 0.035% max

- Silicon (Si): 0.10% min

- Chromium (Cr): 0.40% max

- Copper (Cu): 0.40% max

- Nickel (Ni): 0.40% max

- Molybdenum (Mo): 0.15% max

- Vanadium (V): 0.08% max

Mechanical Properties

The mechanical properties of ASTM A106 steel pipes produced by Womic Steel are as follows:

- Tensile Strength: 415 MPa min

- Yield Strength: 240 MPa min

- Elongation: 30% min

asd (2)

Inspection Requirements

ASTM A106 steel pipes produced by Womic Steel are subject to stringent inspection requirements, including visual inspection, dimensional inspection, mechanical testing, hydrostatic testing, and non-destructive testing, to ensure their quality and performance.

Application Scenarios

ASTM A106 steel pipes produced by Womic Steel are widely used in various industries, including:

- Oil and gas

- Power generation

- Chemical processing

- Petrochemical

- Construction

- Shipbuilding

Womic Steel's Production Strengths and Advantages

Womic Steel has a strong production capability and several advantages, including:

- Advanced Production Equipment: Womic Steel is equipped with advanced production equipment, ensuring high-quality and efficient production of ASTM A106 steel pipes.

- Strict Quality Control: Womic Steel implements strict quality control measures at every stage of the production process to ensure that ASTM A106 steel pipes meet the highest quality standards.


Post time: Mar-21-2024